Practical Formula of PVC Products (3)

PVC high filling wood plastic

PVC 100, lead salt compound stabilizer 5.6, foaming modifier (100) 11, Monoglyceride 4.0, PE wax 1.2, stearic acid 0.5, wood powder 30, calcium powder 200, AC foaming agent 2.0, pigment proper amount, recycled material 60.

  

PVC wood-plastic wallboard

1. PVC-8 25, tubing material 100, light calcium 50, wood powder 7, CPE 5, recycled material 25, lead salt stabilizer 1.8, foaming regulator (100/418/80) 5, AC 0.35, white foaming 0.6, PE wax, stearic acid 0.6, pigment proper amount.

 

2. PVC-8 50, light calcium 50, wood powder 5, CPE 3, recycled material 30, lead salt stabilizer 3.0, foaming regulator (100/418/80) 6, AC 0. 55, white foaming 0. 5, PE wax 0. 5, stearic acid 0. 6, pigment proper amount.

 

3. Tubing material 75, light calcium 50, recycled material 50, wood powder 8, PVC 12.5, stabilizer 2.0, foaming regulator (100/418/80) 6-8, AC 0.6, white foaming 1.0, PE wax 0.3, stearic acid 0.5, pigment proper amount.

 

4. PVC-8 75, light calcium 80, wood powder 5, CPE 2, recycled material 25, lead salt stabilizer 4.3, foaming regulator (100/418/80) 6-8, AC 0.6, white foaming 0. 9, PE wax 0. 6, stearic acid 0. 8-1. 2, pigment proper amount.

 

PVC wood plastic door strip

1. PVC 25, tubing material 108, heavy calcium 75, stabilizer 2.5, CPE 4, regulator (90S) 8.0, AC 0.8, PE wax 0.2, stearic acid 0.2.

 

2. PVC 25, light calcium 50, tubing material 50-75, recycled material 25, wood powder 8, PE wax 0.3, stearic acid 0.4, lead salt stabilizer 1.8, AC 0.65, foaming regulator (90S) 3.5.

 

PVC foamed sole

1. PVC 100, DOP 80-85, light calcium 60-65, AC 0.5-0.6, foaming regulator (90S) 2.0, lead salt compound stabilizer 3.8, PE wax 0.6, stearic acid 1.0, color pigment appropriate.

 

2. PVC 100, DOP 90, light calcium 70, AC 0.8, foaming regulator (90S) 2.0, lead-salt compound stabilizer 4.0, PE wax 0.8, stearic acid 1.2, color pigment appropriate.

 

3. PVC 100, DIBP 85, light calcium 60, AC 0.5, foaming regulator (90S) 2.0, calcium-zinc composite stabilizer 4.0, PE wax 0.2, stearic acid 0.3, and color pigment appropriate.

 

Flame retardant and environmental protection cable material

1. Protective cover: PVC 100, TOTM 50, epoxy soybean oil 5, chlorinated paraffin 8, antimony trioxide 5, antioxidant 0.5, calcined ceramsite 5.0, light calcium 10, calcium zinc stabilizer 7, PE wax 0.2, stearic acid 0.3.

 

2. Insulating material: PVC 100, TOTM 45, epoxy soybean oil 3, chlorinated paraffin 8, antimony trioxide 4, antioxidant 0.4, calcined ceramsite 10, light calcium 15, calcium zinc stabilizer 7, PE wax 0.25, stearic acid 0.3.

  

PVC heat shrink film

PVC 50, calcium stearate 0.3, stearic acid 0.25, ACR (20/175) 0.3-0.8, nanometer calcium 0.3, paraffin 0.25, DOP 2.5, soybean oil 2, barium chromium-zinc stabilizer 1.6 (or organotin 1.3), whitening agent 0.005.

 

PVC heat-shrinkable tube

PVC (SG-6/7) 100, light calcium 10, lead salt stabilizer 3. 0, CPE6-8, DOP 5, paraffin 0. 3, stearic acid 0. 6, colormasterbatch right amount.